ইঞ্জিনিয়ারিং মেটেরিয়ালস MCQ
321. For one cubic metre of brick masonry, the number of bricks required is-
400
450
500
550
ব্যাখ্যা: [Note: মেট্রিক ইট 500টি লাগে।
322. The final setting time of ordinary cement should not be more than-
2 hours,
4 hours
4 hours
10 hours
323. The normal consistency of Portland cement is about-
10%
15%
20%
25%
324. The time required for seasoning of timber in kiln seasoning is-
2 to 5 days
5 to 10 days
10 to 20 days
20 to 40 days
325. The percentage of the slag component of Portland-slag cement varies from-
10 to 40%
70 to 80%
40 to 70%
80 to 90%
326. The main constituent of Portland cement is-
lime
iron oxide
alumina
alkalies
327. Lime occurs in a free state in nature.
True
False
328. The commonly used lime in white washing is---
quick lime
fat lime
lean lime
hydraulic lime
329. The amount of gypsum usually added in the manufacture of cement is-
0.5 to 1%
3 to 5%
1 to 3%
0.1 to 0.5%
330. The cementing property in cement is mainly due to---
lime
silica
iron oxide
alumina
331. The compressive strength of ordinary cement is less than its tensile strength
right
wrong
332. The initial setting time of rapid hardening cement should not be less than--
30 min
4 hours
1 hour
10 hours
333. In brick field, pugmill is used for- [BPSC-22]
preparation of clay
drying of bricks
burning of bricks
moulding of bricks
ব্যাখ্যা: ব্যাখ্যা: A pugmill or pug mill is a machine in which clay or other materials are mixed into a plastic state. A pugmill
may be a fast continous mixer.
334. যদি বালুর FM ৩.০ হয় তবে উক্ত বালুকে বলা হয়-
very fine sand
fine sand
medium sand
flaky
335. Initial setting time (minimum) of ordinary port land cement is- [BPSC-22]
60 minutes
45 minutes
30 minutes
20 minutes
ব্যাখ্যা: ব্যাখ্যা: Initial setting time (minimum) of ordinary portland cement is 30 minutes and final setting time 10 hours.
336. The moisture content in timber for framework should not exceed-
5%
10%
15%
20%
337. The fuel generally used for burning limestone is
coalur
firewood
charcoal
any one of these
338. The silica in Portland cement should be
10 to 20%
20 to 25%
25 to 40%
40 to 60%
ব্যাখ্যা: ব্যাখ্যা: ১। ক্যালসিয়াম অক্সাইড (CaO)..........63%
২। ম্যাগনেশিয়াম অক্সাইড (MgO)..........2%
৩। সিলিকা (SiO₂)..........22%
৪। অ্যালুমিনা (Al2O3)..........7%
৫। আয়রন অক্সাইড (Fe2O3)..........3%
৬। সালফার ট্রাই-অক্সাইড (SO3).........2%
৭। ক্ষারকীয় পদার্থ...........1%
........ মোট 100%
339. The compressive strength of paving bricks should not be less than-
20 MN/m²
30 MN/m²
40 MN/m²
50 MN/m²
340. ইটের Herring-bone bond গাঁথুনি কোন কাজে ব্যবহৃত হয়?
Brick paving
Very thick wall
Partition walls
Footing foundation